Hot rolled aluminum sheet factorycan manufacturing high fine warm rolling aluminum sheet plate product with rapid pace. The heated aluminum ingot is rolled on the roller table through more than one passes of reversible rolling to a thickness of 18~25mm, and then double-coiled reversible type completing rolling, after 3 to five passes, the thickness of aluminum sheet can reach 2.5 mm. The production potential can attain 150kta. This configuration is the fine configuration for decent rolling turbines. In addition to the immature production technology of cans, it may produce various aluminum sheet & plate and strips.
When the new rolled aluminum sheet manufacturing facility is heaten the aluminum plate processed, the coarse dendrites and numerous inclusions in the as-forged metal billet are elongated along the deformation route, so that the dense inclusions among the as-cast metal dendrites are progressively organized in a fibrous form along the deformation path. Warmth remedy can not do away with or trade the streamline distribution in the workpiece. The blessings of warm rolled aluminum sheetare:1, warm rolling can remodel the as-solid shape with decrease plasticity to the deformed shape (processing shape) with better plasticity, which can significantly improve the processing overall performance of the aluminum sheet metallic.2, commonly, the deformation resistance of the metal decreases with the growth of temperature, so the deformation resistance of the metallic all through hot rolling is lower than that in bloodless rolling, which can considerably reduce the power intake during rolling.3, as the temperature rises, the plasticity of the aluminum sheetincreases, so the plasticity of the metallic during hot rolling is better, this is to say, the processing performance of the aluminum metal is higher, so that a larger quantity of deformation can be used for rolling, and the aluminum also can be reduced. The threshold cracking and fracture lack of the aluminum sheet metal can improve the yield price of the metallic.Four, due to the fact the steel has higher plasticity and smaller deformation resistance throughout warm rolling, hot rolled aluminum sheet factorycan use large ingots, which cannot most effective boom productivity and yield, increase rolling velocity, however additionally create a continuity and automation of the rolling system condition.